1. Nhọrọ akụrụngwa na Fraịm
Osisi silk
Na-eji polyethylene (PO), polypropylene (PP) ma ọ bụ niylon (PA), ma họrọ ihe ahụ dịka ebumnucheSpornsna-akachasị anya, ma na-eyi mmiri na-eguzogide mmiri bụ pa).
Tinye ihe mgbakwunye dị ka Masterbatch, mgbochi ultraviolet (UV), na-ere ezumike, wdg, ma gwakọta ha nke ọma site na igwefoto dị elu.
Akụrụngwa ahụ na-akpọnwụ iji wepu mmiri (okpomọkụ 80-100 ℃, oge 2-4 awa).
Iberibe akwa na ihe nrapado
Ntọala akwa ahụ na-eji polypropylene (PP) akwa na-enweghị akpali ma ọ bụ akwa mpempe akwụkwọ, nke ga-enwerịrị iguzogide na nguzogide.
Ihe nrapado na-abụkarị polyurethane (PU) ma ọ bụ Styrene-Belrene Latex (SBR), na ụfọdụ ngwaahịa ngwaahịa dị elu na-eji ihe nrapado gburugburu.
2. Ntughari na udiri ahihia yarn
Mmiri na-agbaze
Ihe a gwakọtara agwakọta na-agbaze ma gbazee site na mkpụrụ osisi cracder (ọnọdụ okpomọkụ 160-220 ℃), na ahịhịa na-atọgbọ yarn site na isi dị larn site na isi dị larịị.
A na-emepụta ọtụtụ ahịhịa yarn n'otu oge site na iji ọtụtụ isi oghere, ya na obosara nke 0.8-1m na ọkpụrụkpụ nke 0.05-0.15mm.
Na-agbatị na curling
A na-agbatị ahịhịa yarn ugboro 3-5 iji bulie ike ya ogologo oge, mgbe ahụ ọ na-etolite site na ikuku na-etolite iji mepụta mmiri / spal.
Clearder Creater na-ekewa ahịhịa yarn n'ime otu filaments otu ma na-efegharị ha na spindle maka iji ya.
3. Tufung na-egbu egbu
A na-etinye akwa ahụ na igwe
A na-eji mkpọchi akwa ahụ emeghe, a na-agbasa ya na ebe ị na-aga (dị ka KH550) iji melite ndọpụta nke gluu.
Ikike ọrụ
Use a double needle bed tufting machine, with a needle speed of 400-1200 needles/minute and an adjustable row spacing of 3/8″-5/8″.
A na-akụ ahịhịa yarn n'ime ntọala ntọala dị ka preset njupụta (6500-21000 agịịrị / ㎡), enwere ike ịhazi ahịhịa dị elu site na 10-60mm.
Recatezọ a na-enyocha agịga agịga (20-50N) iji zere ịgba akwụkwọ actigage, na yarn ịgbanwe sistemụ yarn.
4..
Ibe mkpuchi mbu
Denye 2-3mm Styrene-Booday Latex (ọdịnaya siri ike 45-60%) site na spraying ma ọ bụ spraying ma ọ bụ ịgbatị oghere nke isi.
Infrared tupu ihicha (80-100 na-ewepụ 60% nke mmiri.
Agbanwe agbamume nke abụọ
Mpempe akwụkwọ na-ejikọ fiber meplesh akwa ma ọ bụ poyester ma ọ bụ ntuli aka iji bulie nguzosi ike.
Tinye gluu polyurethane (ọkpụrụkpụ 1.5-2.5mm), ma jiri usoro ntụgharị ugboro abụọ iji hụ na edo edo edo.
Na-agwọ ma na-akpụ akpụ
Ihulata: Oge mbido 50-70 ℃ (20-30min), ọkwa ikpeazụ 110-130 ℃ (15-25min).
Ike ya nke ihe nrapado ga-abụrịrị ≥35n / cm (encon Standard).
5. Usoro na-emecha
Ahihiachacha
Ahịhịa ahịhịa nke ọma combs ahịhịa nnyapade iji hụ na ọnụego kwụ ọtọ karịa 92%.
Ihe okirikiri na-eme ka igwe na-acha uhie uhie na-enwe ndidi na-ejide onwe ya nke ± 1mm, na laser statemeter ozugbo.
Usoro ọgwụgwọ
Ọgwụgwọ antistatic: Spraying Sonviam Sin Quinium Sonvelọ Ọrụ (nguzogide uru ≤10 ^ 9.
Ikike mkpuchi dị jụụ: elu nke ahịhịa na-eme ka ọ bụrụ titanium dioxide / ngwakọta si titanidi / na ọdịiche okpomọkụ na-belata nke okpomoku site na 3-5 ℃.
Nnyocha nyocha dị mma
Ule ule (usoro tabur, 5000 nke iyi <5%)
Nnwale A Na-amụ Eri (Quv 2000
Mmetụta Mmetụta (Vertical Ngbanwe 4-9mm, n'ahịrị na Standards FIFA)
6. Slitting na nkwakọ ngwaahịa
Vetikal na kehoraizin na-efegharị
Onye na-agbasa ikuku na-agbasasị-axis maka iweghachi, ọkọlọtọ na-eme ka obosara 4m.
Igwe okirikiri okirikiri dị elu na-efe efe (izi ezi ± 0.5cm), sistemụ akpaaka na-akpaghị aka na-edekọ ozi banyere.
Nchịkwa, nchekwa na ụgbọ njem
Ihe nkiri na-etinye ihe nkiri Payfrof Kraft Kraft composite nkwari ngwaahịa, a na - etinye okpu iche na nsọtụ abụọ nke ogwe.
E kwesịrị ichebe nchekwa site na ọkụ na mmiri (iru mmiri ≤ 60%), na ịdị elu na-agbada ruo 5 n'ígwé.
7. Usoro pụrụ iche (nhọrọ)
3d Lawn: Tordinary TughaIji mepụta akụkụ dị elu / obere ahịhịa, jikọtara ya na ịpị ọkụ na-acha ọkụ.
Sistemụ ahịhịa a gwakọtara ọnụ: Ihe mejupụtara ya na 10-20% sitere na ahịhịa ahịhịa etinyere.
Ahịhịa Smartn: Croven Fiber Fiber oyi akwa, okpomoku na iru mmiri na-arụ ọrụ.
Usoro ahụ na-ekpuchi usoro nrụpụta site na akụrụngwa iji mezue ngwaahịa. A na-ahazi paramita niile dị ka ISO 9001 naStorslọ Ọrụ Turf Council (STC), enwere ike idozi usoro usoro dị ka ọnọdụ ngwa ụfọdụ akọwapụtara.
Oge post: Feb-12-2025